目的 研究可用于工业包装的秸秆纤维栈板。方法 通过对1/4栈板进行建模和有限元分析， 而后用一定配比的秸秆纤维浆通过半湿压工艺对其进行试制， 并对其进行最大压力和耐破强度试验。结果 该方案测试结果与软件分析的结果比较接近， 栈板的最大压力可达7424 N， 材料的耐破极限达到2.833 MPa。结论 通过有限元分析与试验验证， 文中设计的栈板能够满足使用要求， 且承重为750kg， 该设计方案可行。

The aim of this work was to study straw fiber pallet that could be used for industrial packaging. After modeling and finite element analysis of the 1/4 pallet, trial production was carried out using a certain proportion of straw fiber pulp by the semi-wet compression process. The maximum pressure and bursting strength tests were also performed. It was found that the test results were relatively close to the results of the software analysis. The maximum pressure of the pallet was 7424 N, and the breaking resistance limit of the material reached 2.833 MPa. The finite element analysis and experimental verification demonstrated that the pallet designed in this paper could meet the operating requirements, and it could support a weight of 750 kg. The design scheme was feasible.