为了了解高强瓦楞复合纸板侧压性能，采用夹层结构材料侧压性能的测试方法对其进行了实验测试。实验选用了10，15，20和30 mm 4种厚度的高强瓦楞复合纸板样品，分别按照横向和纵向进行了测试。结果表明：相同厚度纸板纵向的侧压强度大于横向；不同厚度纸板随着纸板厚度的增加，横向和纵向侧压强度都呈降低趋势。研究结果对于提高高强瓦楞复合纸板托箱的堆码承载能力，具有很强的实践应用价值。

In order to understand edgewise compression properties of high-strength composite corrugated cardboard, the edgewise compression test for sandwiched structure was applied to the composite corrugated cardboard. High-strength composite corrugated specimens with four kinds of thickness, 10, 15, 20 and 30mm were selected to test in accordance with longitudinal and transverse direction, respectively. The results showed that the edgewise compression test value in the longitudinal direction is greater than that in transverse one for the cardboard with the same thickness; with the thickness increase of composite corrugated cardboard, the edgewise compression strength in longitudinal and transverse directions both tends to decrease. The test results for high-strength composite corrugated cardboard are of significant application in practice, especially for improving stack bearing capacity of pallet container.