目的 以明胶和预胶化淀粉为原料制备具有缓冲效果的生物质可降解泡沫材料，为缓冲包装用生物质泡沫提供一种新的选择。方法 通过对不同明胶-淀粉质量比、固含量、十二烷基硫酸钠(SDS)用量进行实验研究，并进行结构表征及静态压缩性能测定对泡沫材料进行综合评价。结果 得到了明胶-淀粉缓冲泡沫材料的最优条件，固含量(用质量分数表示)为20%，表面活性剂质量分数为0.75%，明胶-淀粉质量比为70∶30。在此最优条件下的明胶-淀粉缓冲泡沫材料发泡倍率为5.14倍，表观密度为0.064 g/cm³，弹性模量为36.64 kPa，50%抗压强度为2.49 kPa。结论 以明胶和预胶化淀粉为原料制备的复合泡沫材料具有表观密度低、缓冲性能较好的特点。单因素实验结果表明，预胶化淀粉对泡沫的力学性能有增强作用。

Using gelatin and pregelatinized starch as raw materials to prepare biodegradable foam materials with cushioning effect, which provides a new option for biomass foam for cushioning packaging. Through the experimental study of different gelatin starch mass ratio, solid content and twelve alkyl sulfate (SDS) dosage, the structural characterization and static compression properties of the foam materials were comprehensively evaluated. The composite foams prepared from gelatin and pregelatinized starch have low apparent density and good cushioning properties. The single factor experiment showed that starch had a strong mechanical effect on foam. The optimum conditions for gelatin starch buffer foam are solid content 20%, surfactant content 0.75%, gelatin Starch Ratio 70∶30. Under the optimal conditions, the foaming ratio of gelatin starch buffer foam is 5.14 times, the apparent density is 0.064 g/cm3, the elastic modulus is 36.64 kPa, and the 50% compressive strength is 2.49 kPa.